IES 8422 Inter-Mix 90 Hybrid Panel Bonding Adhesive Urethane/Epoxy 6.76 OZ

Description

IES 8422 Inter-Mix 90 Panel Bonding Adhesive is chemically engineered to be one of the best panel bonders on the market today.
Epoxy Resin and Polyamid Hardner System:
Provides lap shear strengths of greater than 3,000 psi. on steel and aluminum substrates.
90 Minute Work Time:
Provides ample time for application,  panel alignment and clamping.
Heat Cure Activator:
Built into the formula provides
Heat Induced Curing
for faster fixture times if desired.
Adhesion Promoter:
Built into the formula provides stronger bonding to steel, aluminum, SMC and FRP.
Urethane and ATBN Copolymer Resins:
Built into the formula, provides Impact and Fracture Resistance, even at lower temperatures.
High Performance Fillers:
Provide easier pumping and non-sag performance, even when heat induce curing is needed.
Solid Glass Beads:
Are added in to prevent adhesive squeeze out when clamping and provide a consistent bond line thickness.
INTER-MIX 90
Hybrid Panel Bonding Adhesive
A heavy-bodied two-part high strength epoxy/urethane adhesive that will bond to a wide variety of metal and plastic substrates.
When used according to specific directions IES Hybrid Panel Bonding Adhesive may be used in the replacement of:
Quarter Panels
Door SkiNS
Roof Panels
Truck Box Sides and other Outer Body Sheet Metal.
Do not use on structural components such as: Rails, Rocker Panels
Core Supports,
Pillars, etc
• 2:1 Cartridge
• High Strength Bond
• Reduces Welding Time
• Reduces Fire Risks
• Provides Corrosion Protection
• Contains Glass Beads to Maintain A Constant Bondline Thickness.
• Bonds & Seals Simultaneously
• Weld-Through When Using Squeeze-Type Resistance Spot Welding
• Reduces Warpage
• Lifetime Limited Warranty when used as per directions.
TYPICAL PROPERTIES
Temperature *Working Time: 70°F - 80°F 60-90 Minutes
De-Clamping Time: 70°F - 80°F 6-8 Hours 100° F 3 Hours 140° F 60 Min. 180° F 30 Min.
T
otal Cure Time: 24 Hours
Working /De-Clamping time may be accelerated when used in conjunction with heat.
Please refer to the “Weld Bonding Procedures or SMC Bonding Procedures” for more information.
Lap Shear Strength Test
ASTM-D-1002 Average Substrates:
Cold Rolled Steel 3500 psi
Aluminum 3500 psi